6011 Welding Rod
Category: Carbon steel welding rod with cellulose potassium coating.
Origin: Zhejiang, China
Implementation standard: AWS A5.1
Product detailed
|
Place of Origin: Zhejiang, China (Mainland) |
Brand Name: Ocean welding |
Model Number: Welding electrode e6011 |
|
Diameter:2.0mm 2.5mm 3.2mm 4.0 5.0mm |
Length: 300mm-350mm |
Material:Welding electrodes price |
|
Operating Current: AC/DC |
Welding Current: 25-200A |
Operating Temperature:Normal |
|
Application: Low carbon steel structure |
Color: grey-white/blue |
Application:building and general machinery |
|
Product Name: Welding Electrodes AWS E6011 |
Standard: AWS A.5.1 E6011 |
Certification: ISO CE |
|
Advantage: Easy Restrike Arc |
OEM: Accept OEM |
Feature: High welding efficiency |
Description
E6011 is a special carbon steel electrode for vertical downward welding with high cellulose potassium coating. AC and DC dual purpose, it has the characteristics of beautiful shape and high welding efficiency during vertical downward welding. Welding rod swing should not be too wide, and the arc height should be appropriate
APPLICATION:
Suitable for butt joint, corner joint and lap welding of thin plate structures, such as low-carbon steel structure of power station flue, air duct, transformer mailbox, hull and vehicle outer plate
Application
Suitable for butt joints, corner joints and lap welds of sheet metal structures. Such as power station flue, duct, transformer tank, hull and vehicle outer panel of low carbon steel structure.
Deposited metal mechanical properties
| Test Item | Rm/MPa | ReL/MPa | A(%) | KV2/J(-30℃) |
|
GV |
≥420 | ≥330 | ≥22 | ≥27 |
| Test Value | 480-580 | ≥340 | 22-26 | 100-130 |
Reference Current
| Diameter(mm) | 2.0 | 2.5 | 3.2 | 4.0 | 5.0 | |
| Welding Current(A) | 25-40 | 30-50 | 70-100 | 90-140 | 150-200 | |
Key points of welding operation
- Welding rod angle: adjust the welding rod angle according to the welding position. When welding horizontally, the angle between the welding rod and the welding direction is maintained at 60° - 80°; when welding vertically, the angle between the welding rod and the surface of the weldment is about 90°, and the molten pool is controlled by appropriate swinging; when welding horizontally and overhead, reduce the angle between the welding rod and the weldment to prevent the molten iron from falling.
- Arc length: maintain short arc welding, and try to control the arc length to be close to the diameter of the welding rod to enhance the arc stability, reduce the intrusion of air into the molten pool, and improve the quality of the weld. Welding speed: maintain an appropriate welding speed to avoid too fast to cause poor fusion, or too slow to cause overheating and deformation of the weld. Usually controlled at 10 - 25cm/min, it can be flexibly adjusted according to the weld formation.
FAQ
Q: What materials are suitable for welding with 6011 electrodes?
A: It is mainly used for welding various types of low-carbon steel and some low-alloy steel. It is suitable for building steel structures, automobile manufacturing, mechanical processing, ship pipelines and other fields. It also has good adaptability to rusty and oily steel surfaces.
Q: Does 6011 electrode need to be baked before welding?
A: It is recommended to bake at 70-150℃ for 0.5-1 hour to remove moisture and prevent pores. After baking, place it in an insulation cylinder for use.
Q: Should I choose AC or DC power when welding?
A: 6011 electrodes can be used for both AC and DC. It is recommended to use reverse connection (the electrode is connected to the positive pole and the workpiece is connected to the negative pole) for DC welding to obtain better arc stability and penetration depth; when using AC power, normal welding can also be guaranteed.