Stainless Steel Welding Rod AWS E308-16
DESCRIPTION:
a. Stainless steel welding rod E308-16 weld metal(19Cr-9Ni)is austenite structure,it has excellent mechanical properties and shows good resistance to intergranular corrosion.
b. It can be used for all position welding with excellent performance:stable arc,small spatters,good appearance of weld.And also the welding electrode shows good heat-resistance character,not easy to turn red and gas porosity is not produced.
APPLICATION:
Stainless steel welding rod E308-16 can be used for welding 18Cr-8Ni(A1S1304),A1S1301,SUS308,etc.
ATTENTION:
a.Before welding,stainless steel welding rod E308-16 welding electrodes should be baked at the temperature from 300-350℃ for one hour.
b.Using stainless steel brush to clean the weld seam,in order to avoid scrap iron entering and affect its quality.
Chemical Composition of Deposited Metal: （%）
C | Mn | Si | P | S | Cr | Ni | |
Standard | 0.052 | 0.86 | 0.65 | 0.020 | 0.010 | 19.30 | 10.05 |
Typical | ≤0.08 | 0.5-2.5 | ≤0.90 | ≤0.040 | ≤0.030 | 18.0-21.0 | 9.0-11.0 |
Mechanical Properties of Deposited Metal
Tensile Strength | Elongation | |||||||
σb(Mpa) | δ5 (%) | |||||||
Standard | 620 | 47 | ||||||
Typical | ≥550 | ≥35 | ||||||
Recommended Current(AC or DC*) | ||||||||
Size(mm) | Φ2.5×350 | Φ3.2×350 | Φ4.0×400 | Φ5.0×400 | ||||
Flat Current(A) | 50-85 | 80-120 | 100-150 | 140-180 | ||||
Vertical,Overhead | 45-80 | 70-110 | 90-135 | - | ||||
Current(A) | ||||||||
![ZTG~PS4N)DW[B9801_40]2B](/Content/uploads/20212134/202105131653266b263a33cc4b4d4f9312fe899bd5c306.png "ZTG~PS4N)DW[B9801_40]2B")
Hot Tags: stainless steel welding rod aws e308-16, China, manufacturers, suppliers, factory, company, wholesale, discount, buy, low price, high quality, products
Previous
No InformationYou Might Also Like
Send Inquiry