SS Electrode E308L-16
Brand Name: Ocean Welding
Model: E308l-16
Material: Stainless Steel
Diameter: 2.0mm 2.5mm 3.2mm 4.0mm ...
Information of product E308L-16
|
Place of Origin: Zhejiang, China (Mainland) |
Model Number: AWS E308L-16 |
Brand Name:Dayang/Ocean Welding |
|
Diameter:2.0MM,2.5MM,3.2MM,4.0MM |
Length: 300mm-500mm |
Material: Stainless Steel |
|
Operating Current: International Standard |
Welding Current: International Standard |
Operating Temperature: lower than 300°C |
|
Supply Ability:200 Ton/Tons per Month |
Port:Shanghai/Ningbo |
Both AC and DC |
| AWS Standard:AWS A5.4 | Trade term: CIF FOB DDU |
SS Electrode E308L-16
Packaging & Delivery
| Packaging Details: |
1.1kg per plastic box or 5kgs per plastic box(shrink bag+pvc box) 2. 4 plastic boxes(20kgs)/carton 3. 50 carton(1 ton)/pallet |
SS Electrode E308L-16
Chemical composition of deposited metal(%)
| C | Mn | Si | S | P | Cr | Ni | Mo | Cu |
| ≤0.04 | 0.5-2.5 | ≤0.9 | ≤0.03 | ≤0.04 | 18-21 | 9-11 | ≤0.75 | ≤0.75 |
SS Electrode E308L-16
About us
1.We are Hangzhou Lin an Dayang Welding Material Co., Ltd., one of leading manufacturing enterprises in China, specialized in making consumables like welding electrodes, welding wire for 20 years.
2.With experienced and skilled technicians who engaged in this industry for about 20 years, we have a professional production line for welding electrode E308L-16 now.
Application
Vehicles, bridge-engineering, machine-engineering, steel structures, shipping manufacture, building and containers.
More about stainless steel welding electrodes
When chrome-nickel stainless steel is repeatedly heated during welding, it will precipitate carbides, which will reduce corrosion resistance and mechanical properties. Therefore, chrome-nickel stainless steel welding should be properly selected according to the working conditions of the equipment (working temperature, medium type, etc.).
In order to prevent intergranular corrosion caused by heating, the current should not be too large when welding, generally about 20% lower than carbon steel electrode, while the arc should not be too long, the layer is fast cold, and the narrow bead is suitable.
All kinds of stainless steel welding rods should be kept dry during use. The welding rods should be baked before welding (the drying can not be repeated many times, otherwise the coatings are easy to crack and peel off), to prevent the welding rods from sticking oil and other dirt, so as to avoid the increase of deposited metal. Carbon content and influence welding quality
Precautions and FAQs
- Storage: sealed and moisture-proof, relative humidity ≤ 60%112.
- Prohibited scenarios: not suitable for martensitic or duplex stainless steel, E316L-16 is recommended for welding 316L base material114.
- Welding rod damp: performance needs to be tested after drying, and the electrode should be discarded if the coating falls off1.
- Vertical welding molten pool drops: reduce the current by 10-15%, and use the segmented de-welding method1.